2.5.2 Non‐biobased Fillers/Reinforcements with Biobased Polymers
The development of biobased composites, in which non‐biobased additives or fillers are reinforced with the biobased polymers has been restricted to the addition of reinforcements to PLAs [48, 49]. When PLA is reinforced with fillers such as hydroxyapatite fibers (HAF) (up to 60 wt%), there is a significant improvement in their Young's modulus under compression molding conditions at 180 °C. The maximum value of Young's modulus attained was about 10 GPa for PLA/HAF composites [49]. For heavily loaded composites, a brittle behavior was observed and a covalent fiber–matrix interaction was revealed [49]. When PLA has been reinforced with carbon nanotubes (CNTs), there occurs a significant rise in the Young's modulus and hardness of the composites [50]. Purified CNTs are able to better disperse in a PLA matrix than nonpurified CNTs, thus resulting in better thermomechanical properties.
2.5.3 Biobased Filler/Reinforcement and Biobased Polymer
Biobased composites with natural fiber reinforcements have several advantages over those with synthetic reinforcements and has become one of the most popular research topics of the decade. Further, natural polymers derived from renewable resources are ecofriendlier and less expensive compared to synthetic polymers. Hemp, keratin, pure cellulose fibers, and flax are used to produce composites with very good dampening properties and high flexibility [51, 52]. In the current research scenario, focus is on enhancing the fiber–resin interactions, neglecting fiber orientation. The poor uniformity in the fiber length and orientation in biobased composites results in huge variations in the mechanical properties of similar samples and hence represents one of the major limitations for its use as a commercial product. Researchers are carrying out both physical and chemical surface treatments for presenting them successfully in the market as a competitive alternative to synthetic fibers. Each component in the natural fiber composite has been separated and studied individually for optimizing the fiber–matrix interactions and also to completely understand their physical properties. Thermotreatment [53], calendaring [54], fiber stretching [55], and electric discharge [56] are some of the common optimization methods available. The methods indicated herein are used to improve the surface of the fibers physically on a macroscale and they do not alter or induce any chemical changes in the fibers. In some cases, they could also be used to improve the adhesion with the polymer matrix and also fiber orientation. Shorter fibers from high cellulose content fibers and plant particulates could be filtered by using Solvent extraction technique.
In some cases, in order to improve the fiber–matrix interactions, the chemical treatment of the fibers is also carried out. Alkaline treatments of fibers can be used as a pretreatment method in addition to the chemical modifications that are carried out. Alkalis like sodium hydroxide could be used for treating the fibers in which the cellulose lattice is converted into a more stable form [57]. It has been found that the mechanical properties of flax/epoxy polymers are increasing at a significant rate than the nontreated samples after alkaline treatment [58]. On the other hand, if there is no stretching of the fibers during the NaOH/water alkaline treatment, then it results in the shrinkage of the fibers [59]. Water can be substituted with ethanol for overcoming this problem [59]. Another method used for enhancing the interfacial adhesion between the reinforcements and the polymer matrix is the use of coupling agents, such as organosilanes which is a common chemical modification method [60]. Even though there occurs a decrease in the crystallinity of the reinforcements, there is still an increase in the tensile properties of the PLA/wood flour composites. Morphological analysis also proves that there is a stronger interfacial bonding that occur in the developed composites.
2.6 Conclusion
It is a well‐known fact that the research activities related to the development of novel biobased polymers have been increasing drastically over the past few decades. Nowadays, the trend has changed from using simpler systems having thermoplastic materials reinforced with natural fibers to more advanced composites with carefully engineered biobased matrices or which are completely of biobased origin (i.e. both the matrix and reinforcements are biobased). Advancements in the polymer and composite processing techniques have led to significant progress in the development of novel biobased composites, which have both industrial and commercial applications. PLA and PLA‐based composites are the most predominating materials used as biobased biomedical equipment, as there is only little focus or work done in other materials such as hydrogels, which are used as scaffolds in cell growth and tissue regeneration. Expectations are in such a way that the development of novel biobased polymers will continue its ladder climbing as it finds more interesting applications in the biomedical field, especially for cell scaffolding and drug delivery, as reported in this chapter.
References
1 1 Alghazali, K.M., Nima, Z.A., Hamzah, R.N. et al. (2015). Bone‐tissue engineering: complex tunable structural and biological responses to injury, drug delivery, and cell‐based therapies. Drug Metab. Rev. 47 (4): 431–454.
2 2 Langasco, R., Spada, G., Tanriverdi, S.T. et al. (2016). Bio‐based topical system for enhanced salicylic acid delivery: preparation and performance of gels. J. Pharm. Pharmacol. 68 (8): 999–1009.
3 3 Render, D., Rangari, V.K., Jeelani, S. et al. (2014). Biobased calcium carbonate (CaCO3) nanoparticles for drug delivery applications. Int. J. Biomed. Nanosci. Nanotechnol. 3 (3): 221–235.
4 4 Awal, A., Rana, M., and Sain, M. (2014). Thermorheological and mechanical properties of cellulose reinforced PLA bio‐composites. Mech. Mater. 80: 87–95. https://doi.org/10.1016/j.mechmat.2014.09.009.
5 5 Boumhaout, M., Boukhattem, L., Hamdi, H. et al. (2017). Thermomechanical characterization of a bio‐composite building material: mortar reinforced with date palm fibers mesh. Constr. Build. Mater. 135: 241–250.
6 6 Oliver‐Ortega, H., Granda, L.A., Espinach, F.X. et al. (2016). Tensile properties and micromechanical analysis of stone groundwood from softwood reinforced biobased polyamide11 composites. Compos. Sci. Technol. 132: 123–130.
7 7 Shibata, S., Cao, Y., and Fukumoto, I. (2008). Flexural modulus of the unidirectional and random composites made from biodegradable resin and bamboo and kenaf fibres. Compos. Part A 39: 640–646.
8 8 Arao, Y., Fujiura, T., Itani, S., and Tanaka, T. (2015). Strength improvement in injection‐molded jutefiber‐reinforced polylactide green‐composites. Compos. Part B 68: 200–206.
9 9 Khan, Y.H., Islam, A., Sarwar, A. et al. (2016). Novel green nano composites films fabricated by indigenously synthesized graphene oxide and chitosan. Carbohydr. Polym. 146: 1–466. https://doi.org/10.1016/j.carbpol.2016.03.031.
10 10 Mohanty, A.K., Misra, M., and Drzal, L.T. (2002). Sustainable bio‐composites from renewable resources: opportunities and challenges in the green materials world. J. Polym. Environ. 10 (1/2): 19–26.
11 11 Idicula, M., Sreekumar, P.A., Joseph, K., and Thomas, S. (2009). Natural fiber hybrid composites – a comparison between compression molding and resin transfer molding. Polym. Compos. 30: 1417–1425. https://doi.org/10.1002/pc.20706.
12 12 Sreekumar, P.A., Joseph, K., Unnikrishnan, G., and Thomas, S. (2007). A comparative study on mechanical properties of sisal‐leaf fibre‐reinforced polyester composites prepared by resin transfer and compression moulding techniques. Compos. Sci. Technol. 67: 453–461.
13 13 Kim, K.‐W., Lee, B.‐H., Kim, H.‐J. et al. (2012). Thermal and mechanical properties of cassava and pineapple flours‐filled PLA bio‐composites. J. Therm. Anal. Calorim. 108: 1131–1139.
14 14 Feldmann, M. and Bledzki, A.K. (2014). Bio‐based polyamides reinforced with cellulosic fibres – processing and properties. Compos. Sci. Technol. 100: 113–120.
15 15