PVP, poly‐n‐vinylpyrrolidone; ME, microemulsion; IW, incipient wetness.
Mean Au particle size, calculated by counting particles in high‐resolution TEM images of many different regions, is the crucial factor in determining activity. Results from recycled Au55‐based catalysts confirm that deactivation does not occur. All reactions were carried out at 100 °C in toluene.
a Catalyst preparation: Au55, Au55 preparation.
b Exact loading was determined using inductively coupled plasma mass spectroscopy.
c For full statistical breakdown of particle size distributions.
The importance of efficient activation of cluster‐based catalysts for CO oxidation was highlighted by a study that compared ligand removal using ozone exposure against a rapid thermal treatment for catalysts containing Au13[PPh3]4[S(CH2)11CH3]4 (8 Å diameter) ligand‐protected clusters on titania (anatase phase) [68]. The authors demonstrated that ozone treatment, followed by calcination at 400 °C for two hours in air, resulted in the most active catalyst, which had smaller gold particles compared with the less active catalyst treated by calcination alone.
The team of Professor Tsukuda used [Au11(PPh3)8Cl2]Cl, mentioned earlier [27], to prepare a series of mesoporous silica‐supported catalysts for oxidation of alcohols. The authors reported the importance of using a mixture of solvents (80% dichloromethane and 20% ethanol) in order to achieve homogeneous dispersion of clusters over a large surface area by optimizing the solvent‐mediated interaction of cluster with support [69]. Heat treatment at 200 °C produced active catalysts with Au clusters of ∼1 nm confined within a high surface area mesoporous silica support (SBA‐15) [69]. In another excellent study, the same team used hydroxyapatite (Ca10(PO4)6(OH)2) as a support for a range of thiol‐protected gold clusters Aun (n = 10, 18, 25, 39). The authors pinpointed a maximum of activity with an impressive turnover frequency (TOF) of 18 500 h−1 per Au atom at n = 39 in solvent‐free peroxide‐initiated aerobic selective (∼99%) oxidation of cyclohexane to cyclohexanol and cyclohexanone [70]. The use of hydroxyapatite prevented cluster aggregation due to strong interaction between the Au clusters and PO43− moieties. However, it proved impossible to differentiate catalysts with respect to cluster sizes since, in all samples, these appeared to be around 1 ± 0.5 nm in size even when sophisticated high‐angle annular dark field‐scanning TEM was used at moderate to high magnifications. This observation was explained by formation of “an ensemble of structural isomers produced in the calcination of Aun(SG)m,” which “will give rise to polydisperse TEM images.” Aberration‐corrected electron microscopy studies of pure Au144 supported on ultrathin carbon film, followed by reconstruction of obtained data, allowed construction of 3D electron density maps of such clusters [71]. Atomically resolved structures of Au9 clusters supported on TiO2 nanosheets (Figure 5.6) obtained using aberration‐corrected electron microscopy were successfully matched with structural isomers of supported clusters predicted by high‐level quantum mechanical calculations [72].
Figure 5.6 High‐resolution electron microscopy images (a1–c1) and (a2–c2) of Au9 clusters deposited on titania nanosheets under optimized imaging conditions. The scale bar is 0.5 nm. Panels I, III, and IV show the density functional theory (DFT) models for three isomers of Au9.
Source: Al Qahtani et al. 2016 [72]. Reproduced with permission of American Institute of Physics. (See online version for color figure).
The smallest clusters are not always the most active species, where, in the case of benzyl alcohol oxidation, larger particles are more active: “unexpectedly, Au∼144 and Au∼330 on hierarchically porous carbon exhibited significantly higher turnover frequency than Au25 and Au38” [73]. In fact, use of Au9 cluster‐based catalysts, which gradually evolved toward larger sizes, allowed us to establish a particle size effect in solvent‐free aerobic oxidation of cyclohexene – we showed that catalytic activity appeared only after Au0 particles larger than 2 nm had formed [74]. Such particle growth was observed only in the presence of trace amounts of peroxide species in the cyclohexene (stabilizer‐free reagent), highlighting the sensitivity of such catalysts in terms of particle size stability to the reaction media. This study also demonstrated that conventional bright‐field TEM is unsuited for the imaging of clusters on SiO2 NPs due to the poor contrast with the supported sub‐1 nm Au clusters. X‐ray photoelectron spectroscopy can be used to pinpoint the presence of clusters on supports since the characteristic electron binding energy is shifted to higher values in the case of ultrasmall clusters (regardless of their origin – made under UHV or chemically synthesized) [39].
Interestingly, even for the seemingly similar in nature Aun(SG)m clusters (n = 10, 15, 18, 22, 25, 29, 33, 39), only some of the clusters (n = 10, 15, 18, 25, 39) proved to be stable with respect to aggregation during activation, while others (n = 22, 29, 33) produced larger aggregates under the same activation conditions [75]. Although catalysts with “as‐deposited” clusters had higher catalytic activity than the pure support, the removal of ligands resulted in about fourfold increase in the H2 production rate. Similarly, about fourfold higher activity of a Au10‐cluster‐based catalyst was observed in comparison with catalysts made using large Au NPs.
In cases of relatively weak affinity between clusters and surface of support, fabrication of catalysts with reasonably high metal loadings may require a special approach of adding a non‐solubilizing (for cluster) solvent to the deposition mixture. For example, in the case of deposition of the Au9 on WO3 for loadings greater than 0.1 wt%, n‐hexane was slowly added to the mixture